玉米秸秆基吸油材料的制备与表征

doi:10.3969/j.issn.0253-2417.2016.05.006

摘要/Abstract

摘要： 以玉米秸秆（RCS）为原料，经氨水预处理得预处理玉米秸秆（PCS），再经乙酸酐酯化改性制备改性玉米秸秆（ECS）吸油材料，并考察不同酯化条件对产物吸油性能的影响。结果表明：RCS、PCS（预处理6 h）对0^#柴油的吸收倍率分别为1.90和4.43 g/g；以冰乙酸为溶剂，冰乙酸与乙酸酐质量比为1：1，秸秆与冰乙酸-乙酸酐混合液的质量比为1：15，催化剂浓硫酸用量为4.5%（以秸秆质量计），反应温度为110℃条件下，酯化反应5 h所得改性产物ECS的吸油率可达9.03 g/g，且ECS疏水性和漂浮性能均得到显著改善。采用XRD、FT-IR、SEM和BET等方法对预处理前后及酯化改性后秸秆进行了分析与表征。结果表明：酯化反应已顺利进行，酯化改性后秸秆呈非晶态，ECS呈均匀的介孔结构，介孔及粗糙表面的出现提高了材料的吸油率和漂浮性能。

关键词: 玉米秸秆, 酯化改性, 吸油材料

Abstract: By using raw corn stalk (RCS) as staring material, PCS was pretreated with ammonia water and then employed to perform esterification with acetic anhydride. Thus, the oil absorbent materials derived from raw corn stalk (ECS) was obtained. The effect of esterification condition on the performance of oil absorption was also investigated. The results indicated that the oil absorbency of the RCS and PCS (pretreated for 6 h) to 0^# diesel were 1.90 and 4.43 g/g, respectively. The oil absorbency of the obtained ECS material could be 9.03 g/g which was prepared under the following esterification conditions:acetic acid as solvent, m(acetic acid):m(acetic anhydride)=1, m(corn stalk):m(liquid mixture)=1:15,4.5% H₂SO₄ as catalyst (base on the mass of PCS), reaction temperature 110℃ and reaction time 5 h. The obtained ECS displayed a remarkably increase in hydrophobicity and floating ability after esterification modification. The RCS, PCS and ECS were analyzed and characterized by BET, FT-IR, XRD, SEM. The results showed that the esterification reaction was carried out smoothly. the corn stalk after esterification modified presents amorphous state. and ECS even exhibits mesoporous structure. Additionally, the appearances of mesoporous structure and rough morphology were helpful to improve the oil absorbency and floating ability of the ECS.

Key words: corn stalk, esterifying modification, oil absorbent material

中图分类号:

TQ35

刘晓晖, 曹亚峰, 李沅, 刘兆丽, 谭凤芝. 玉米秸秆基吸油材料的制备与表征[J]. 林产化学与工业, 2016, 36(5): 37-44.

LIU Xiao-hui, CAO Ya-feng, LI Yuan, LIU Zhao-li, TAN Feng-zhi. Preparation and Characterization of Oil Absorbent Material Derived from Corn Stalk[J]. Chemistry and Industry of Forest Products, 2016, 36(5): 37-44.

参考文献

[1] 崔明,赵立欣,田宜水,等.中国主要农作物秸秆资源能源化利用分析评价[J].农业工程学报,2008,24(12):291-296. CUI Ming,ZHAO Li-xin,TIAN Yi-shui,et al.Analysis and evaluation on energy utilization of main crop straw resources in China[J].Transactions of the CSAE,2008,24(12):291-296.
[2] 孙明湖,咸惠军,南方,等.大工业应用是解决秸秆问题的根本途径[J].中国生态农业学报,2005,13(3):35-37. SUN Ming-hu,XIAN Hui-jun,NAN Fang,et al.The industrial utilization is the essential way to solve the problem of agricultural stalks[J].Chinese Journal of Eco-Agriculture,2005,13(3):35-37.
[3] IVSHINA I B,KUYUKINA M S,KRIVORUCHKO A V,et al.Oil spill problems and sustainable response strategies through new technologies[J].Environment Science:Processes Impacts,2015,17(7):1201-1219.
[4] LIN Jin-you,SHANG Yan-wei,DING Bin.et al.Nanoporous polystyrene fibers for oil spill cleanup[J].Marine Pollution Bulletin,2012,64(2):347-352.
[5] DENIZ C,SAADET D,BURAK K,et al.Evaluation of butyl rubber assorbent material for the removal of oil and polycyclic aromatic hydrocarbons from seawater[J].Environmental Science & Technology,2009,43(10):3846-3852.
[6] DONG Xiao-chen,CHEN Jun,MA Yan-wen,et al.Superhydrophobic and superoleophilic hybrid foam of graphene and carbon nanotube for selective removal of oils or organic solvents from the surface of water[J].Chemical Communications,2012,48(86):10660-10662.
[7] ZHU Xiao-tao,ZHANG Zhao-zhu,REN Gui-na,et al.A novel superhydrophobic bulk material[J].Journal of Materials Chemistry,2012,22:20146-20148.
[8] DUTTA K,PRAMANIK A.Synthesis of a novel cone-shaped CaAl-layered double hydroxide (LDH):Its potential use as a reversible oil sorbent[J].Chemical Communications,2013,49(57):6427-6429.
[9] JIANG Lei,ZHAO Yong,ZHAI Jin.A lotus-leaf-like superhydrophobic surface:A porous microsphere/nanofiber composite film prepared by electrohydrodynamics[J].Angewandte Chemie,2004,116(33):4338-4341.
[10] LIM T T,HUANG X.Evaluation of kapok (Ceiba pentandra (L.) Gaertn.) as a natural hollow hydrophobic-oleophilic fibrous sorbent for oil spill cleanup[J].Chemosphere,2007,66(5):955-963.
[11] 崔美,黄仁亮,苏荣欣,等.木质纤维素新型预处理与顽抗特性[J].化工学报,2012,63(3):677-687. CUI Mei,HUANG Ren-liang,SU Rong-xin,et al.An overview on ligncellulose pretreatment and recalcitrant characteristics[J].Journal of Chemical Industry and Engineering (China),2012,63(3):677-687.
[12] 彭丽,刘昌见,刘百军,等.水稻秸秆蒸汽爆破-酯化改性制备吸油材料[J].化工学报,2015,66(5):1854-1860. PENG Li,LIU Chang-jian,LIU Bai-jun,et al.Steam explosion and esterification modification of rice straw for oil spill absorption material[J].Journal of Chemical Industry and Engineering (China),2015,66(5):1854-1860.
[13] 朱超飞.玉米秸秆的化学改性、表征及吸油性能的研究[D].广州:华南理工大学硕士学位论文,2012. ZHU Chao-fei.The study of characteristics and oil absorption of chemically modified corn stalks[D].Guangzhou:Master Degree Thesis of South China University of Technology,2012.
[14] 李龙,盛冠忠.X射线衍射法分析棉秆皮纤维结晶结构[J].纤维素科学与技术,2009,17(4):37-40. LI Long,SHENG Guan-zhong.Analysis on crystalline structure of cellulose fiber from cotton-straw bast by X-ray diffraction method[J].Journal of Cellulose Science and Technology,2009,17(4):37-40.
[15] LI Man-man,PAN Hong-chuan,HUANG Sui-liang,et al.Controlled experimental study on removing diesel oil spillages using agricultural waste products[J].Chemical Engineering Technology,2013,36(4):673-680.
[16] 张建兴,陈洪章.秸秆醋酸纤维素的制备[J].化工学报,2007,58(10):2548-2552. ZHANG Jian-xing,CHEN Hong-zhang.Preparation of cellulose acetate from crop straw[J].Journal of Chemical Industry and Engineering (China),2007,58(10):2548-2552.
[17] 刘黎阳,郝学密,刘晨光,等.瞬间弹射蒸汽爆破联用化学法预处理玉米秸秆的组分和酶解分析[J].化工学报,2014,65(11):4557-4563. LIU Li-yang,HAO Xue-mi,LIU Chen-guang,et al.Evaluation of instant catapult steam explosion combined with chemical pretreatments on corn stalk by components and enzymatic hydrolysis analysis[J].Journal of Chemical Industry and Engineering (China),2014,65(11):4557-4563.
[18] 陈嘉川.造纸植物资源化学[M].北京:科学出版社,2012:78-80. CHEN Jia-chuan.Papermaking Plant Resource Chemistry[M].Beijing:Science Press,2012:78-80.
[19] 李丹.以玉米秸秆为原料的天然吸油材料制备及性能分析[D].天津:天津大学硕士学位论文,2013. LI Dan.Preparation and characterization of the natural oil sorbents from corn straw[D].Tianjin:Master Degree Thesis of Tianjin University,2013.
[20] ZHANG Xi,SHI Feng,NIU Jia,et al.Superhydrophobic surfaces:From structural control to functional application[J].Journal of Materials Chemistry,2008,18(6):621-633.
[21] 戴光泽,陈德,倪庆清,等.植物炭材料的柴油吸附性能[J].西南交通大学学报,2006,46(1):20-24. DAI Guang-ze,CHEN De,NI Qing-qing,et al.Diesel oil sorption behaviours of plant charcoals[J].Journal of Southwest Jiaotong University,2006,46(1):20-24.