聚乳酸/三聚氯氰改性木粉/油胺复合材料的制备及表征

杨琳强1, 吴美婷1, 金立维1,2   

  1. 1. 中国林业科学研究院 林产化学工业研究所;生物质化学利用国家工程实验室;国家林业局 林产化学工程重点开放性实验室;江苏省生物质能源与材料重点实验室, 江苏 南京 210042;
    2. 中国林业科学研究院 林业新技术研究所, 北京 100091
  • 收稿日期:2016-11-09 出版日期:2017-06-25 发布日期:2017-07-03
  • 通讯作者: 金立维,副研究员,博士,硕士生导师,主要从事生物质材料与水性胶黏剂的研究;E-mail:liwei-jin@163.com E-mail:liwei-jin@163.com
  • 作者简介:杨琳强(1991-),男,江苏太仓人,硕士生,主要从事生物质高分子材料的研究
  • 基金资助:
    中国林科院林产化学工业研究所团队建设创新工程项目(LHSXKQ6)

Preparation and Characterization of Poly (Lactic Acid)/Wood Flour Modified with Cyanuric Chloride/Oleyl Amine Composites

YANG Linqiang1, WU Meiting1, JIN Liwei1,2   

  1. 1. Institute of Chemical Industry of Forest Products, CAF;National Engineering Lab. for Biomass Chemical Utilization;Key and Open Lab. of Forest Chemical Engineering, SFA;Key Lab. of Biomass Energy and Material, Jiangsu Province, Nanjing 210042, China;
    2. Research Institute of Forestry New Technology, CAF, Beijing 100091, China
  • Received:2016-11-09 Online:2017-06-25 Published:2017-07-03

摘要: 使用三聚氯氰(TCT)对原料杨木粉(RWF)进行改性,并使用改性木粉(TWF)与油胺(OAM)在聚乳酸(PLA)体系下反应后挤出制备复合材料。红外光谱表明:TCT的三嗪环结构连接到了木粉上,在反应挤出过程中,TWF接枝上了OAM。元素分析和滴定分析表明:TWF增加的氮元素与氯元素的物质的量比为2.91:1,TCT上3个活性氯中的两个参与了反应。OAM加入导致PLA产生了降解,但复合材料PLA/TWF/OAM降解弱于PLA/RWF/OAM;在相同OAM用量下,PLA/TWF/OAM拉伸强度和弯曲强度均优于PLA/RWF/OAM;在相同木粉用量下,PLA/TWF/OAM的熔体流动速率大于PLA/RWF。动态力学性能分析表明:在相同OAM用量下,PLA/TWF/OAM与PLA/RWF/OAM相比具有较高的玻璃化转变温度。

关键词: 三聚氯氰, 木粉, 油胺, 聚乳酸, 熔体流动性能

Abstract: Raw wood flour (RWF) was modified with cyanuric chloride (TCT), and the modified wood flour (TWF) and oleyl amine (OAM) were used to prepare composites with poly(lactic acid) by reactive extrusion. FT-IR spectra indicated that the structure of TCT was attached to wood flour and OAM was grafted onto TWF in the progress of reactive extrusion. Elemental analysis and titration analysis showed that the molar ratio of nitrogen and chlorine of TWF was 2.91:1 and two of three active chlorine of TCT were involved in the reaction. The addition of OAM led to the degradation of PLA. However, the degradation of PLA/TWF/OAM composites was weaker than that of PLA/RWF/OAM composites. PLA/TWF/OAM composites exhitbited better tensile strength and flexural strength than that of PLA/RWF/OAM composites under the same dosage of OAM. PLA/TWF/OAM composites had a greater melt flow rate than that of PLA/TWF composites under the same dosage of wood flour. DMA revealed that PLA/TWF/OAM composites had a higher glass transition temperature than that of PLA/RWF/OAM composites under the same dosage of OAM.

Key words: cyanuric chloride, wood flour, oleyl amine, poly(lactic acid), melt flow property