原位合成炭基磷钨酸及其催化性能初探

卢燕凤1, 吴耿烽1, 曾常伟1, 李涛2, 吕建华1, 陈燕丹1, 黄彪1   

  1. 1. 福建农林大学 材料工程学院, 福建 福州 350002;
    2. 福建农林大学 生命科学学院, 福建 福州 350002
  • 收稿日期:2014-08-16 出版日期:2015-08-25 发布日期:2015-08-29
  • 通讯作者: 黄彪(1966—),教授,博士生导师,主要从事生物质材料的研究;E-mail:fjhuangbiao@hotmail.com。 E-mail:fjhuangbiao@hotmail.com
  • 作者简介:卢燕凤(1990—),女,福建泉州人,硕士,主要从事生物质能源与炭材料的研究;E-mail:lyf1990fj@126.com
  • 基金资助:
    国家林业局948项目(2014-4-30);国家自然科学基金资助项目(31170520);福建省科技计划项目(2013H0004)

In-situ Synthesis and Catalytic Properties of Carbon-based Phosphotungstic Acid

LU Yan-feng1, WU Geng-feng1, ZENG Chang-wei1, LI Tao2, LÜ Jian-hua1, CHEN Yan-dan1, HUANG Biao1   

  1. 1. College of Material Engineering, Fujian Agriculture and Forestry University, Fuzhou 350002, China;
    2. College of Life Science, Fujian Agriculture and Forestry University, Fuzhou 350002, China
  • Received:2014-08-16 Online:2015-08-25 Published:2015-08-29

摘要: 以杉木屑为原料,采用原位合成法制备炭基磷钨酸催化剂,以此催化剂催化水解微晶纤维素制备纳米纤维素(NCC),考察了液料浸渍比、炭化温度及炭化时间等催化剂的制备因素对NCC得率的影响。结果表明:液料浸渍比2.5:1(mL:g),炭化温度350 ℃,炭化时间1.5 h条件下制备得到的炭基磷钨酸的催化性能较好,NCC得率可达25.28 %。采用傅里叶红外光谱仪、热重分析及扫描电镜对炭基磷钨酸催化剂进行了表征,结果表明:磷钨酸较好地负载在炭材料上,炭基磷钨酸的Keggin结构特征吸收峰并未发生明显变化,磷钨酸Keggin结构开始分解的温度是370 ℃。用透射电子显微镜和X射线衍射仪对NCC的形貌、晶体结构进行了分析,结果表明:NCC呈棒状,直径9~70 nm,长度130~830 nm,平均长径比为11.2:1,结晶度为76.1 %,平均晶粒尺寸6.9 nm。

关键词: 炭基, 磷钨酸, 催化, 纤维素水解, 纳米纤维素晶体

Abstract: Carbon-based phosphotungstic acid (H3PW12O40) catalyst was prepared from sawdust of Chinese fir by in-situ synthesis. Nanocrystalline cellulose (NCC) from cellulose by catalytic hydrolysis was studied. The effects of impregnation ratio, carbonization temperature and carbonization time on the yield of NCC were also analyzed. The results showed that under the impregnation ratio of liquid to solid 2.5:1, thecarbonization temperature 350 ℃ and carbonization time 1.5 h, a comparatively high yield of NCC was observed as 25.28%. The catalysts were characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis, and scanning electron microscope. The results indicated that phosphotungstic acid was loaded on the carbon under good conditions, the keggin structure characteristic absorption peak of carbon-based phosphotungstic acid remains stable, and the initial decomposition temperature of keggin structure of phosphotungstic acid is 370 ℃. The morphological and crystal structures of NCC were carried out by Transmission electron microscopy and X-ray diffraction. The results showed that the NCC observed by TEM turned out to be rod-like, with the size of 9-70 nm in width and 130-830 nm in length and the average aspect ratio of 11.2:1. X-ray diffraction analysis revealed that the crystallinity of the NCC was 76.1 %, with the average particle size of 6.9 nm.

Key words: carbon-based, phosphotungstic acid, catalysis, cellulose hydrolysis, nanocrystalline cellulose