木质素磺酸钠基膨胀阻燃聚氨酯泡沫的制备及性能

doi:10.3969/j.issn.0253-2417.2021.05.005

Abstract

Abstract:

Sodium lignosulfonate based intumescent flame retardant polyurethane foam(PUF) composite was prepared by one-step foaming method with using sodium lignosulfonate(SLS) as physical filler, the compound of ammonium polyphosphate(APP) and pentaerythritol(PER) as intumescent flame retardant(IFR). Limiting oxygen index(LOI) test was used to study the flame retardancy of PUF materials; thermogravimetric analysis(TG) and cone calorimetry(CONE) were used to analyze the thermal degradation behavior and combustion behavior of PUF materials; scanning electron microscope(SEM) was used to analyze the micro morphology of residual carbon of PUF composites after cone test; the compressive strength of the materials as tested by universal mechanical testing machine. The results showed that LOI value of flame retardant PUF material reached 25.5%, when the amount of SLS was 4% and 30% IFR with the mass ratio of APP to PER of 4:1 was added, the compressive strength of the material was increased to 359.87 kPa. Compared with the pure PUF materials, the maximum thermal degradation rate, heat release rate and total heat release of the flame retardant PUF decreased, and the char yield at 700℃ increased to 34.5%. In sum, the addition of SLS and IFR significantly improved the flame retardant properties and compressive strength.

Key words: polyurethane foam, sodium lignosulfonate, intumescent flame retardant, flame retardancy, combustion behavior

CLC Number:

TQ35

Yue MA, Xu LI, Zhiming LIU. Preparation and Properties of Sodium Lignosulfonate Based Intumescent Flame Retardant Polyurethane Foam[J]. Chemistry and Industry of Forest Products, 2021, 41(5): 31-37.

Figures/Tables 8

Table 1

Table 2

Fig.1

Table 3

Fig.2

Table 4

Fig.3

Table 5

References 16

1	朱吕民, 刘益军. 聚氨酯泡沫塑料[M]. 北京: 化学工业出版社, 2005.
	ZHU L M , LIU Y J . Polyurethane Foam Plastics[M]. Beijing: Chemical Industry Press, 2005.
2	王靖宇, 郝建薇. 无卤阻燃硬质聚氨酯泡沫塑料的研究进展[J]. 中国塑料, 2020, 34 (5): 107- 114.
	WANG J Y , HAO J W . Research progress in Halogen-free flame-retardant RPUF[J]. China Plastics, 2020, 34 (5): 107- 114.
3	YUN G W , LEE J H , KIM S H . Flame retardant and mechanical properties of expandable graphite/polyurethane foam composites containing iron phosphonate dopamine-coated cellulose[J]. Polymer Composites, 2020, 41 (7): 2816- 2828. doi: 10.1002/pc.25578
4	CHEN Y , LI L , WU X . Construction of an efficient ternary flame retardant system for rigid polyurethane foam based on bi-phase flame retardant effect[J]. Polymers for Advanced Technologies, 2020, 31 (12): 3202- 3210. doi: 10.1002/pat.5045
5	张琪, 刘娟, 桑晓明, 等. 高岭土/聚磷酸铵阻燃硬质聚氨酯-酰亚胺泡沫塑料的制备与性能[J]. 材料工程, 2017, 45 (414): 27- 33.
	ZHANG Q , LIU J , SANG X M , et al. Preparation and properties of rigid polyurethane-imide foams flame retarded by Kaolin/APP[J]. Journal of Materials Engineering, 2017, 45 (414): 27- 33.
6	THIRUMAL M , KHASTGIR D , SINGHA N K , et al. Effect of expandable graphite on the properties of intumescent flame-retardant polyurethane foam[J]. Journal of Applied Polymer Science, 2010, 110 (5): 2586- 2594.
7	LIU L , LYU R . Synthesis of a DOPO-triazine additive and its flame-retardant effect in rigid polyurethane foam[J]. e-Polymers, 2019, 19 (1): 235- 243. doi: 10.1515/epoly-2019-0024
8	ZHANG Z, LI D, XU M, et al. Synthesis of a novel phosphorus and nitrogen-containing flame retardant and its application in rigid polyurethane foam with expandable graphite[J/OL]. Polymer Degradation and Stability, 2020, 173: 1-11[2020-12-01]. https://doi.org/10.1016/j.polymdegradstab.2020.109077.
9	CHEN M J , SHAO Z B , WANG X L , et al. Halogen-free flame-retardant flexible polyurethane foam with a novel nitrogen-phosphorus flame retardant[J]. Industrial & Engineering Chemistry Research, 2012, 51 (29): 9769- 9776.
10	ZHANG K, HONG Y, WANG N, et al. Flame retardant polyurethane foam prepared from compatible blends of soybean oil-based polyol and phosphorus containing polyol[J/OL]. Journal of Applied Polymer Science, 2018, 135(5): 1-10[2021-01-10]. https://doi.org/10.1002/app.45779.
11	李旭, 刘志明. 膨胀石墨阻燃碱木质素聚氨酯泡沫的制备及其性能[J]. 功能材料, 2019, 50 (5): 116- 121.
	LI X , LIU ZH M . Preparation and properties of alkali lignin-based polyurethane foam with expanded graphite[J]. Journal of Functional Materials, 2019, 50 (5): 116- 121.
12	杨晓慧, 周永红. 木质素聚氨酯泡沫的研究进展[C]//第三届全国生物质材料科学与技术学术研讨会论文集. 黄山: [s.n.], 2009.
	YANG X H, ZHOU Y H. Research progress of lignin polyurethane foam[C]//International Symposium on Biomass Material Science & Technology. Huangshan: [s.n.], 2009.
13	MOHAMMADPOUR R, SADEGHI G M M.Potential use of black liquor as lignin source for synthesis of polyurethane foam[J/OL]. Journal of Polymer Research, 2020, 27(12): 1-12[2020-12-10]. https://doi.org/10.1007/S10965-020-02334-8.
14	李旭, 周家兴, 刘志明. 膨胀阻燃碱木质素聚氨酯泡沫的制备及性能[J]. 塑料, 2018, 47 (6): 91- 95.
	LI X , ZHOU J X , LIU Z M . Preparation and property of alkali lignin-based polyurethane foam with intumescent flame retardant[J]. Plastics, 2018, 47 (6): 91- 95.
15	鲁晓杰, 汪闯, 刘思源, 等. 膨胀石墨阻燃碱木质素-聚氨酯泡沫性能研究[J]. 塑料科技, 2019, 47 (1): 22- 26.
	LU X J , WANG C , LIU S Y , et al. Study on performance of expandable graphite flame-retarded alkali lignin-polyurethane foam[J]. Plastics Science and Technology, 2019, 47 (1): 22- 26.
16	王佳楠, 边勇军, 羿颖, 等. 碱木质素/聚磷酸铵膨胀阻燃聚氨酯泡沫的制备及性能研究[J]. 塑料科技, 2019, (7): 42- 45.
	WANG J N , BIAN Y J , YI Y , et al. Study on preparation and properties of PUF intumescent flame retarded by alkali lignin/APP[J]. Plastics Science and Technology, 2019, (7): 42- 45.

样品 samples	SLS添加量/% additive amount of SLS	LOI/%
PUF	0	19.1
PUF/2%SLS	2	19.6
PUF/4%SLS	4	19.8
PUF/6%SLS	6	19.6
PUF/8%SLS	8	19.4
PUF/10%SLS	10	19.2

样品 samples	IFR添加量/% additive amount of IFR	LOI/%
PUF/4%SLS/5%IFR	5	21.8
PUF/4%SLS/10%IFR	10	22.8
PUF/4%SLS/15%IFR	15	23.7
PUF/4%SLS/20%IFR	20	24.5
PUF/4%SLS/25%IFR	25	24.7
PUF/4%SLS/30%IFR	30	25.5

样品 samples	T_i/℃	第一阶段first stage		第二阶段second stage		残炭量(700℃)/% char yield
样品 samples	T_i/℃	R_p/(%·min^-1)	T_p/℃	R_p/(%·min^-1)	T_p/℃	残炭量(700℃)/% char yield
PUF	239.2	-6.6	325.9	-2.6	400.5	21.1
PUF/4%SLS	243.3	-6.4	328.3	-2.5	400.2	21.9
PUF/4%SLS/30%IFR	238.2	-6.2	314.8	-1.3	439.8	34.5

样品 samples	点燃时间/s ignition time	第一个峰the first peak		第二个峰the second peak		总热释放量/ (MJ·m^-2) total heat release	残炭量/% char residues
样品 samples	点燃时间/s ignition time	热释放速率/(kW·m^-2) heat release rate	时间/s time	热释放速率/(kW·m^-2) heat release rate	时间/s time	总热释放量/ (MJ·m^-2) total heat release	残炭量/% char residues
PUF	3	215.9	34	—	—	11.4	15.7
PUF/4%SLS	3	206.3	38	—	—	11.0	16.6
PUF/4%SLS/30%IFR	3	152.9	33	158.7	64	9.2	27.5

样品 samples	压缩强度/kPa compressive strength
PUF	229.74
PUF/4%SLS	253.05
PUF/4%SLS/5%IFR	318.36
PUF/4%SLS/10%IFR	355.55
PUF/4%SLS/15%IFR	451.58
PUF/4%SLS/20%IFR	394.56
PUF/4%SLS/25%IFR	376.86
PUF/4%SLS/30%IFR	359.87

Preparation and Properties of Sodium Lignosulfonate Based Intumescent Flame Retardant Polyurethane Foam

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 16

Related Articles 12

Recommended Articles

Metrics

Comments

[1]	Mengke LIANG, Jing CHEN, Peng DAI, Xiaofeng MA, Meng ZHANG, Zhenyang LUO. Preparation and Application of Lignin-based Intumescent Flame Retardant [J]. Chemistry and Industry of Forest Products, 2021, 41(4): 10-16.
[2]	Jinyu LIU, Ruixia LIU, Pingping DENG, Dexiang LIU, Meng GUO, Zhiping WU. Preparation of Lignin-based Ion-imprinted Polymer and Its Adsorption Properties on Cr(VI) [J]. Chemistry and Industry of Forest Products, 2021, 41(2): 24-32.
[3]	Wei ZHOU,Puyou JIA,Meng ZHANG,Yonghong ZHOU. Preparation and Characterization of Nitrogen-containing Heterocyclic Tung Oil-based Rigid Polyurethane Foam [J]. Chemistry and Industry of Forest Products, 2019, 39(2): 53-58.
[4]	HUO Shuping, CHEN Jian, WU Guomin, LIU Guifeng, JIN Can, KONG Zhenwu. Preparation and Properties of Complex Auto-catalytic Polyurethane Foams from Cardanol and Lignin [J]. Chemistry and Industry of Forest Products, 2017, 37(2): 115-120.
[5]	WANG Wan-yu, WANG Dun, ZHANG Yu-cang. Preparation of Polyurethane Foam from Liquefied Rice Straw [J]. Chemistry and Industry of Forest Products, 2015, 35(6): 78-82.
[6]	WEI Bing, CHEN Fan-geng, LI Zhi-hao, CHENG Yuan-chao. Liquefaction of Fermentation Residue of Corn Stover in Polyhydric Alcohols [J]. Chemistry and Industry of Forest Products, 2014, 34(5): 53-59.
[7]	ZHOU Bao-wen, HA Cheng-yong, DENG Lian-li, MO Jian-qiang, SUN Chun-ning, SHEN Min-min. Effect of Ultrasonic Treatment on Physicochemical Properties of Sodium Lignosulfonate [J]. Chemistry and Industry of Forest Products, 2014, 34(2): 67-72.
[8]	XU Li-li;LIAO Bing;NIAN Fu-wei;HUANG Jian-heng;GUO Dou-dou;DENG Mu-jian;PANG Hao. Liquefaction of Bamboo Powder in Polyols and Its Application in Preparation of Semi-rigid Polyurethane [J]. , 2013, 33(6): 48-54.
[9]	LI Chang-yu;LIU Yan-dong;WANG Lei;SHI Jin-jin;LÜCheng-xi. Influence of Alkaline Lignin and Degradation Products of Polyurethane Foam on Structure and Performance of Polyurethane Foam Composite [J]. , 2012, 32(3): 56-60.
[10]	WANG Chun-hai;AI Qing;ZHAO Yin-feng;BEI Ying;FANG Gui-zhen. Adsorption of Copper Ions by Sodium Lignosulfonate-chitosan Polyelectrolyte Complex [J]. , 2012, 32(1): 29-34.
[11]	LI Mei;XIA Jian-ling;YANG Xiao-hua;. Synthesis of Waterborne Epoxy Curing Agent from Sodium Lignosulfonate [J]. , 2011, 31(2): 53-57.
[12]	LIU Li-li;LI Chang-yu. Preparation and Cell Body Structure Property of Reticulated Polyurethane Foam Composites from Ligninsulfonate/Renewable Polyurethane Foam [J]. , 2010, 30(2): 47-51.