生物炭基固体酸的制备及其对合成2-叔丁基对苯二酚的催化性能

doi:10.3969/j.issn.0253-2417.2016.01.010

Abstract

Abstract: Black liquor solid (BLS) and wood meal (WM) were selected as raw materials. The black liquor solid base catalysts (BLSBC) and wood meal base catalysts (WMBC) were prepared by carbonization and sulfonation.The biomass carbon based solid acids were characterized by SEM, TG, FT-IR and elemental analysis.Then these two kinds of the catalysts were applied to synthesize 2-TBHQ.The results showed that the sulfonated biochar catalysts have good thermal stability below 200℃, and successfully grafted with functional group -SO₃H.The increase of carbon content and the decrease exchange capacity of H⁺ were mainly due to the influence of the temperature, and the exchange capacity of H⁺ in wood meal solid acid catalyst was higher than black liquor solid acid catalyst under the same temperature.Conversion of hydroquinone decreased as the exchange capacity of H⁺ decrease, and the selectively of 2-TBHQ was correlated well with the synergetic effect of exchange capacity of H⁺ and content of hydroxyl groups.WMBC-450 exhibited better catalytic selection than commercial solid acid catalysts (amberlyst-15 and 732 ion exchange resin), and the highest selection and yield of 2-TBHQ were 83.8% and 57.6%, respectively.

Key words: black liquor solid, wood meal, catalyze, synthesis, 2-TBHQ

CLC Number:

TQ35

YE Jun, LU Jun-xiang, ZHENG Xian-wei, CHANG Jie, FU Yan. Preparation of Sulfonated Biochar Catalysts and Their Application in 2-TBHQ Synthesis[J]. Chemistry and Industry of Forest Products, 2016, 36(1): 70-76.

References

[1] MELERO J A,VAN GRIEKEN R,MORALES G.Advances in the synthesis and catalytic applications of organosulfonic-functionalized mesostructured materials[J].Chemical Reviews.2006,106(9):3790-3812.
[2] 徐晓维,徐徐,王石发,等.固体酸 Amberlyst-15 催化合成丙烯酸异冰片酯[J].林产化学与工业,2013,33 (3):100-104. XU Xiao-wei,XU Xu,WANG Shi-fa,et al.Synthesis of isobornyl acrylate in the presence of Amberlyst-15[J].Chemistry and Industry of Forest Products,2013,33(3):100-104.
[3] 聂小安,常侠,蒋剑春,等.磁性固体酸催化剂的合成及其酯化催化活性的研究[J].林产化学与工业,2011,31(2):1-6. NIE Xiao-an,CHANG Xia,JIANG Jian-chun,et al.Synthesis of magnetic solid acid catalyst and its catalytic activity for esterification[J].Chemistry and Industry of Forest Products,2011,31(2):1-6.
[4] 刘娣,林鹿,曾珊珊,等.固体酸SO₄^2-/SnO₂催化转化葡萄糖制备乙酰丙酸丁酯[J].林产化学与工业,2013,33(2):66-70. LIU Di,LIN Lu,ZENG Shan-shan,et al.Conversion of glucose into butyl levulinate over solid acid SO₄^2-/SnO₂ catalyst[J].Chemistry and Industry of Forest Products,2013,33(2):66-70.
[5] 余先纯,李湘苏,易雪静,等.固体酸水解玉米秸秆制备糠醛的研究[J].林产化学与工业,2011,31(3):71-74. YU Xian-chun,LI Xiang-su,YI Xue-jing,et al.Hydrolysis of corn stalks for the production of furfural using solid acid as catalyst[J].Chemistry and Industry ofForest Products,2011,31(3):71-74.
[6] LIU Fu-jian,SUN Jing,ZHU Long-feng,et al.Sulfated graphene as an efficient solid catalyst for acid-catalyzed liquid reactions[J].Journal of Materials Chemistry,2012,22(12):5495-5502.
[7] BARBARO P,LIGUORI F.Ion exchange resins:Catalyst recovery and recycle[J].Chemical Reviews,2009,109(2):515-529.
[8] HARA M,YOSHIDA T,TAKAGAKI A,et al.A carbon material as a strong protonic acid[J].A Carbon Material as a Strong Protonic Acid,2004,43(22):2955-2958.
[9] SUGANUMA S,NAKAJIMA K,KITANO M,et al.Hydrolysis of cellulose by amorphous carbon bearing SO₃H,COOH,and OH groups[J].Journal of the American Chemical Society,2008,130(38):12787-12793.
[10] 杨光,王雷波.炭基对甲苯磺酸催化剂在烷基化反应中的研究[J].当代化工,2010,39(1):55-57,77. YANG Guang,WANG Lei-bo.Study on alkylation by carbon-based p-toluene sulfonic acid catalyst[J].Contemporary Chemical Industry,2010,39(1):55-57,77.
[11] 张文娟,马海龙,杨亚提,等.松木粉制备高比表面积炭基固体酸催化剂[J].生物质化学工程,2012,46(1):15-18. ZHANG Wen-juan,MA Hai-long,YANG Ya-ti,et al.Preparation of a carbon-based solid acid catalyst with high specific surface area from pine wood powder[J].Biomass Chemical Engineering,2012,46(1):15-18.
[12] LOU Wen-yong,ZONG Min-hua,DUAN Zhang-qun.Efficient production of biodiesel from high free fatty acid-containing waste oils using various carbohydrate-derived solid acid catalysts[J].Bioresource Technology,2008,99(18):8752-8758.
[13] TIAN Xiao-ning,ZHANG Li-li,BAI Peng,et al.Sulfonic-acid-functionalized porous benzene phenol polymer and carbon for catalytic esterification of methanol with acetic acid[J].Catalysis Today,2011,166(1):53-59.
[14] PARK H W,HONG U G,LEE Y J,et al.Catalytic decomposition of 4-phenoxyphenol to aromatics over palladium catalysts supported on activated carbon aerogel bearing sulfonic acid group[J].Catalysis Communications,2012,20:89-93.
[15] WESSEL R A,BAXTER L L.Comprehensive model of alkali-salt deposition in recovery boilers[J].Tappi Journal,2003,2(2):19-23.
[16] KANG Shi-min,LI Xiang-lan,FAN Juan,et al.Characterization of hydrochars produced by hydrothermal carbonization of lignin,cellulose,D-xylose,and wood meal[J].Industrial and Engineering Chemistry Research,2012,51(26):9023-9031.
[17] 周丽娜,刘可,华伟明,等.碳基磺酸化固体酸材料的制备及其催化性能[J].催化学报,2009,30(3):196-200. ZHOU Li-na,LIU Ke,HUA Wei-ming,et al.Preparation and catalytic performance of sulfonated carbon-based solid acid[J].Chinese Journal of Catalysis,2009,30(3):196-200.
[18] SUGANUMA S,NAKAJIMA K,KITANO M,et al.Hydrolysis of cellulose by amorphous carbon bearing SO₃H,COOH,and OH groups[J].Journal of the American Chemical Society,2008,130(38):12787-12793.
[19] GAGEA B C,PÂRVULESCU A N,PONCELET G,et al.Alkylation of hydroquinone with tert-butanol over silica-immobilized triflate derivatives[J].Catalysis Letters,2005,105(3):219-224.
[20] XU Bing-jun,LI Hui-yun,HUA Wei-ming,et al.MSU-S (BEA) mesoporous molecular sieve:An active and stable catalyst for alkylation of hydroquinone[J].Microporous and Mesoporous Materials,2006,88(1/2/3):191-196.
[21] ZHANG Zheng-bo,ZHOU Fei,NIE Jin.Alkylation of Hydroquinone with tert-butanol catalyzed by polymer-supported sulfonimide[J].Catalysis Letters,2007,119(3/4):271-276.
[22] LIU Ke,LI Cui-can,ZHANG Xiao-hong,et al.Poly (styrene sulfonic acid)-grafted carbon nanotube as a stable protonic acid catalyst[J].Catalysis Communications,2010,12(3):217-221.
[23] LOU Rui,WU Shu-bin.Products properties from fast pyrolysis of enzymatic/mild acidolysis lignin[J].Applied Energy,2011,88(1):316-322.

Preparation of Sulfonated Biochar Catalysts and Their Application in 2-TBHQ Synthesis

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	LU Yanju, ZHAO Zhendong, WANG Jing, XU Shichao, BI Liangwu, CHEN Yuxiang. Synthesis and Biological Activity of Isopimaric Furfural Acylhydrazone Derivatives [J]. Chemistry and Industry of Forest Products, 2019, 39(3): 43-48.
[2]	YANG Xiaohua, ZHU Jinhua, ZHANG Yan, LI Shouhai, LI Mei. Preparation and Properties of Waterborne Epoxy Curing Agents Based on Castor Oil [J]. Chemistry and Industry of Forest Products, 2019, 39(3): 65-71.
[3]	XU Shichao, ZENG Xiaojing, DONG Huanhuan, ZHAO Zhendong. Research Progress in Development and Application of Terpenoid Botanical Herbicides [J]. Chemistry and Industry of Forest Products, 2019, 39(2): 1-8.
[4]	FENG Xuezhen, XIAO Zhuanquan, LU Pingying, FAN Guorong, WANG Zongde. Synthesis and Antibacterial Activity of Hydronopol Dimethyl Alkyl Ammonium Halide [J]. Chemistry and Industry of Forest Products, 2019, 39(1): 35-40.
[5]	TAN Guanni, GAO Yanan, GAO Hong, SHANG Shibin, SONG Zhanqian. Synthesis and Spectra Performance of Dehydroabietic Acid-based Triarylamine with Double Naphthalenes [J]. Chemistry and Industry of Forest Products, 2019, 39(1): 61-66.
[6]	ZHAI Zhaolan, YAN Xinyan, XU Ji, SONG Zhanqian, SHANG Shibin, RAO Xiaoping. Synthesis of Sodium Maleopimaric Acid Long Chain Alkyl (Alkylene) Amines and Their Antifeedant Activity Against Agrotis ypsilon [J]. Chemistry and Industry of Forest Products, 2018, 38(5): 23-29.
[7]	TAO Ran, WANG Chengzhang, ZHANG Changwei, ZHOU Hao, CHEN Hongxia. Synthesis and Antitumor Activity of Selective Oxidation Products of Betulin [J]. Chemistry and Industry of Forest Products, 2018, 38(4): 47-51.
[8]	LI Xiangyu, LI Xueqin, SHI Junyou, LEI Tingzhou. Review on Research Progress of Biomass Carbon-based Magnetic Solid Acid Catalysts [J]. Chemistry and Industry of Forest Products, 2017, 37(5): 9-18.
[9]	ZHANG Rui, DUAN Wengui, LIN Guishan, CHEN Zhicong, HE Ran, LEI Fuhou. Synthesis and Antifungal Activity of Verbenone-based Oxime Sulfonate Compounds [J]. Chemistry and Industry of Forest Products, 2017, 37(5): 68-78.
[10]	LI Qiaoguang, LIU He, SHANG Shibin, SONG Zhanqian. Research Progress of Rosin and Its Derivatives in Polymer Synthesis [J]. Chemistry and Industry of Forest Products, 2017, 37(4): 23-29.
[11]	JIN Linlin, XIAO Zhuanquan, FAN Guorong, CHEN Jinzhu, WANG Peng, WANG Zongde, CHEN Shangxing. Synthesis and Antifungal Activity of Series of N-Hydronopol Pyridine Ammonium Halide [J]. Chemistry and Industry of Forest Products, 2017, 37(3): 122-128.
[12]	ZHU Shouji, YANG Xuebing, XU Shichao, ZHAO Zhendong, JIANG Jianxin. Synthesis and Antibacterial Activity of Bis-alkanoyl-amines Heterocyclic Derivatives of cis-1,8-p-Menthane Diamine [J]. Chemistry and Industry of Forest Products, 2017, 37(2): 79-84.
[13]	MA Yuan, DUAN Wengui, LIN Guishan, LIU Luzhi, HUANG Zhengsong, LEI Fuhou. Synthesis and Biological Activities of Perillaldehyde-based Schiff Base-(thio) urea Compounds [J]. Chemistry and Industry of Forest Products, 2017, 37(1): 54-62.
[14]	TAO Ran, WANG Cheng-zhang, YE Jian-zhong, ZHOU Hao, CHEN Hong-xia. Synthesis and Antibacterial Activity of Nitrogenated and Haloid Derivatives of Ginkgo Biloba Leaves Polyprenol [J]. Chemistry and Industry of Forest Products, 2016, 36(6): 29-34.
[15]	XU Jing-liang, CHEN Xiao-yan, XIAO Shi-yuan, YUAN Zhen-hong. Research Progress on Biosynthesis of Long Chain Fuel Alcohol [J]. Chemistry and Industry of Forest Products, 2016, 36(4): 140-146.