Abstract: Effects of preparation technology of urea-formaldehyde resin modified with melamine(MUF)on property of plywood were studied.Results showed that formaldehyde emission of plywood conformed to E1 degree(≤1.5 mg/L) when formaldehyde/urea molar ratio was 1.1:1 and F/U molar ratio in weak acid stage was lower than 1.6:1.The bond strength of plywood using MUF resin in which content of melamine was beyond 3% did not satisfy to the requirement of type Ⅱ plywood (0.7 MPa).It was possible to decrease formaldehyde emission and improve bonding strength by adding 1% isocyanate curing agent in curing stage.Plywood,decorative plywood and blockboard manufactured with this MUF resin conformed to E1 degree required by standard.
Key words: urea-formaldehyde resin, melamine, formaldehyde emission, hardener, plywood
CLC Number:
TQ433.431
JIN Li-wei;WANG Chun-peng;ZHAO Lin-wu;LIU Yi;JIANG Yu. STUDY ON PREPARATION AND PROPERTIES OF E1-TYPE UF RESIN MODIFIED WITH MELAMINE[J]. , 2005, 25(1): 40-44.
0 / / Recommend
Add to citation manager EndNote|Reference Manager|ProCite|BibTeX|RefWorks
URL: http://www.cifp.ac.cn/EN/
http://www.cifp.ac.cn/EN/Y2005/V25/I1/40