表面活性剂对有机硅包覆松香基环氧树脂微胶囊的影响

doi:10.3969/j.issn.0253-2417.2014.01.005

林产化学与工业 ›› 2014, Vol. 34 ›› Issue (1): 25-30.doi: 10.3969/j.issn.0253-2417.2014.01.005

表面活性剂对有机硅包覆松香基环氧树脂微胶囊的影响

林广沅, 吴国民, 孔振武

中国林业科学研究院林产化学工业研究所; 生物质化学利用国家工程实验室; 国家林业局林产化学工程重点开放性实验室; 江苏省生物质能源与材料重点实验室, 江苏南京 210042

收稿日期:2013-03-22 出版日期:2014-02-25 发布日期:2014-03-05
通讯作者: 孔振武，研究员，博士，博士生导师，主要从事天然资源化学利用及聚合物高分子材料研究；E-mail：kongzhenwu@yahoo.com.cn。 E-mail:kongzhenwu@yahoo.com.cn
作者简介:林广沅（1987-），男，江西吉安人，硕士生，主要从事天然资源化学利用及聚合物材料研究
基金资助:
林业公益性行业科研专项（201104031）

Effects of Surfactants on Silica Encapsulating Maleopimaric Acid Glycidyl Ester Type Epoxy Resin

LIN Guang-yuan, WU Guo-min, KONG Zhen-wu

Institute of Chemical Industry of Forest Products, CAF; National Engineering Lab.for Biomass Chemical Utilization; Key and Open Lab.of Forest Chemical Engineering, SFA; Key Lab.of Biomass Energy and Material, Jiangsu Province, Nanjing 210042, China

Received:2013-03-22 Online:2014-02-25 Published:2014-03-05

摘要/Abstract

摘要： 以马来海松酸酐缩水甘油酯型环氧树脂（MPTGE）为原料与聚乙二醇反应合成了一种与MPTGE具有相似分子结构的松香基非离子型表面活性剂（MP），再以MP及其它5种常用表面活性剂乳化MPTGE作为嚢芯，正硅酸四乙酯（TEOS）为囊壁，采用溶胶-凝胶法制备了一种新型有机硅包覆环氧树脂微胶囊。研究了不同种类及用量的表面活性剂对微胶囊粒径及其分布的影响，并通过光学显微镜、扫描电镜、Zeta粒径测定等分析方法表征了微胶囊的表面形貌、粒径尺寸及分布。结果表明，表面活性剂MP有助于有机硅包覆环氧树脂微胶囊的形成；在MP用量为16.7%（质量分数）时，制备的微胶囊表面光滑致密、分散均匀。

关键词: 表面活性剂, 微胶囊, 有机硅, 马来海松酸, 环氧树脂

Abstract: A novel microcapsule was prepared from silica encapsulating maleopimaric acid glycidyl ester type epoxy resin (MPTGE) by sol-gel process. In these microcapsules system, MPTGE was used as the core material, and tetraethyl orthosilicate(TEOS) acted as the shell material. Some ionic, nonionic, macromolecular surfactants and a rosin-basd surfactant (MP) which was synthesized from MPTGE and polyoxyalkylene were used as the stabilizer. The effects of different surfactants and concentrations on the particle size and distribution of the encapsulated microcapsules were investigated. The surface morphology, particle size and distribution of microcapsules were characterized by optical microscope, scanning electronic microscope and zeta size analyzer, respectively. Experimental results indicated that the surfactant MP synthesized from MPTGE was favorable to form TEOS encapsulating MPTGE microcapsules. The microcapsules had smooth and compact outer surface when the amount of MP was close to 16.7 %.

Key words: surfactant, microcapsules, silicone, maleopimaric acid, epoxy resin

中图分类号:

TQ35

林广沅, 吴国民, 孔振武. 表面活性剂对有机硅包覆松香基环氧树脂微胶囊的影响[J]. 林产化学与工业, 2014, 34(1): 25-30.

LIN Guang-yuan, WU Guo-min, KONG Zhen-wu. Effects of Surfactants on Silica Encapsulating Maleopimaric Acid Glycidyl Ester Type Epoxy Resin[J]. Chemistry and Industry of Forest Products, 2014, 34(1): 25-30.

参考文献

[1] PARK J H, YE M, PARK K.Biodegradable polymers for microencapsulation of drugs[J].Molecules, 2005, 10(1):146-161.
[2] GIRAUD S, BOURBIGOT S, ROCHERY M, et al.Microencapsulation of phosphate:Application to flame retarded coated cotton[J].Polymer Degradation and Stability, 2002, 77(2):285-297.
[3] TONA VÁSQUEZ R V, JIMÉNEZ ESTELLER L, BOJARSKI A D.Multiscale modeling approach for production of perfume microcapsules[J].Chemical Engineering and Technology, 2008, 31(8):1216-1222.
[4] WHITE S R, SOTTOS N R, GEUBELLE P H, et al.Autonomic healing of polymer composites[J].Nature, 2001, 409(6822):794-797.
[5] WANG Chun-shan, SHIEH J Y.Phosphorus-containing epoxy resin for an electronic application[J].Journal of Applied Polymer Science, 1999, 73(3):356-361.
[6] 袁彦超, 容敏智, 章明秋.三聚氰胺-甲醛树脂包裹环氧树脂微胶囊的制备及表征[J].高分子学报, 2008(5):472-480.
[7] ZHANG Huan-zhi, WANG Xiao-dong, WU De-zhen.Silica encapsulation of n-octadecane via sol-gel process:A novel microencapsulated phase-change material with enhanced thermal conductivity and performance[J].Journal of Colloid and Interface Science, 2010, 343(1):246-255.
[8] FANG Gui-yin, CHEN Zhi, LI Hui.Synthesis and properties of microencapsulated paraffin composites with SiO₂ shell as thermal energy storage materials[J].Chemical Engineering Journal, 2010, 163(1/2):154-159.
[9] 沈敏敏, 刘治猛, 哈成勇, 等.马来海松酸缩水甘油酯的合成[J].广州化学, 2001, 26(2):21-26.
[10] 孔振武.马来海松酸类环氧树脂的合成及其表征[D].北京:中国林业科学研究院博士学位论文, 1994.
[11] 倪卓, 杜学晓, 邢锋, 等.表面活性剂对自修复环氧树脂微胶囊的影响[J].深圳大学学报:理工版, 2008, 25(4):351-357.
[12] 李岚, 袁莉, 梁国正, 等.表面活性剂对聚脲甲醛包覆双环戊二烯微胶囊的影响[J].精细化工, 2006, 23(5):429-434.
[13] 刘洋, 黄焕, 孔振武, 等.非离子型水性萜烯基环氧树脂乳化剂的合成与特性[J].林产化学与工业, 2009, 29(5):23-29.
[14] 赵立英, 马会茹, 孙志刚, 等.非离子型活性乳化剂及其水性环氧树脂的制备和性能[J].化学学报, 2010, 68(2):174-180.
[15] 施雪珍, 陈铤, 顾国芳.水性环氧树脂乳液的研制[J].功能高分子学报, 2002, 15(3):306-310.

表面活性剂对有机硅包覆松香基环氧树脂微胶囊的影响

Effects of Surfactants on Silica Encapsulating Maleopimaric Acid Glycidyl Ester Type Epoxy Resin

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

关于本刊

投稿指南

在线期刊

相关单位

联系我们

[1]	李俊杰, 董云, 赵华平, 马红霞. 膦腈环核腰果酚环氧树脂的制备及表征[J]. 林产化学与工业, 2019, 39(4): 100-104.
[2]	吴国民, 陈健, 霍淑平, 刘贵锋, 金灿, 孔振武. 自催化型萜烯基环氧树脂多元醇水分散体的制备与表征[J]. 林产化学与工业, 2019, 39(1): 23-28.
[3]	孙熠昂, 宗传晖, 王飞, 张纳, 李爱香. 马来海松酸环氧树脂在纸基覆铜板中的应用[J]. 林产化学与工业, 2019, 39(1): 123-128.
[4]	马红亮, 陈健, 焦健, 邓拥军, 孔振武, 房桂干. 有机硅氧烷改性杨木纤维的制备及其表征[J]. 林产化学与工业, 2018, 38(6): 20-26.
[5]	陈虹霞, 王成章, 叶建中, 周昊, 陶冉. 漆脂基脂肪粉的制备工艺及性质研究[J]. 林产化学与工业, 2018, 38(6): 67-74.
[6]	翟兆兰, 闫鑫焱, 许吉, 宋湛谦, 商士斌, 饶小平. 马来海松酸长链烷基酰(亚)胺钠的合成及其对小地老虎的拒食活性研究[J]. 林产化学与工业, 2018, 38(5): 23-29.
[7]	张凯强, 唐功文, 闫志山, 马林荣, 黄鑫. 液晶环氧树脂对生物基腰果酚-糠醛树脂性能的影响[J]. 林产化学与工业, 2018, 38(4): 41-46.
[8]	邓叶俊, 黄立新, 张彩虹, 谢普军, 丁莎莎, 王晓杰. 喷雾干燥法制备皱皮木瓜籽油微胶囊及其性能研究[J]. 林产化学与工业, 2018, 38(1): 33-38.
[9]	刘贵锋, 吴国民, 陈健, 孔振武. 有机硅改性没食子酸非异氰酸酯聚氨酯的制备及性能研究[J]. 林产化学与工业, 2018, 38(1): 39-46.
[10]	霍淑平, 陈健, 刘贵锋, 吴国民, 孔振武. 腰果酚基环氧磷酸酯对E-51/IPDA环氧树脂体系性能的影响[J]. 林产化学与工业, 2017, 37(6): 28-34.
[11]	王凤, 龙柱, 陈杰, 王斌, 张凤山. 腰果酚聚氧乙烯醚复配脱墨剂的制备及应用[J]. 林产化学与工业, 2017, 37(6): 95-100.
[12]	刘迪, 吴国民, 刘贵锋, 陈健, 孔振武. 聚硅氧烷改性水性环氧树脂/聚氨酯复合聚合物的制备及性能研究[J]. 林产化学与工业, 2017, 37(5): 39-44.
[13]	闫鑫焱, 饶小平, 宋湛谦, 商士斌. 聚萜烯马来酸酐聚乙二醇酯高分子表面活性剂的制备及性能研究[J]. 林产化学与工业, 2017, 37(2): 129-134.
[14]	宋健, 李梅, 李守海, 黄坤, 夏建陵. 腰果酚二醚曼尼希碱固化剂的合成及其相分离现象研究[J]. 林产化学与工业, 2016, 36(5): 61-67.
[15]	刘迪, 吴国民, 刘贵锋, 孔振武. 阴离子型聚硅氧烷改性萜烯基环氧树脂多元醇水分散体的制备、表征及微观结构[J]. 林产化学与工业, 2016, 36(5): 68-74.