Study on UV Curing Reactivity of Allyl Resinate

LU Yan-ju, ZHAO Zhen-dong, GU Yan, CHEN Yu-xiang, BI Liang-wu, SUI Guan-hua   

  1. Institute of Chemical Industry of Forest Products, CAF;National Engineering Lab.for Biomass Chemical Utilization;Key and Open Lab.on Forest Chemical Engineering, SFA, Nanjing 210042, China
  • Received:2010-02-02 Revised:1900-01-01 Online:2010-06-30 Published:2010-06-30

PDF (PC)

782

摘要： 研究了树脂酸烯丙酯作为单体进行UV光固化反应的影响因素及其固化产物性能。采用红外光谱法对双键转化率进行了表征和分析,并对固化膜性能进行测试。结果表明,双键转化率随光照时间的增加而增加,随引发剂含量增加先上升后下降;固化过程中,表干时间随引发剂用量、光照强度的增加及光照距离的减小而变短,即相对固化速率增加;在较佳条件UV光照距离4.5cm、光照强度100%下,以8%米氏酮(商品名MK)为引发剂、光照时间250s时乙烯基双键转化率为97.9%,以5%2-羟基-2-甲基苯丙酮(商品名Darocure 1173)为引发剂、光照时间300s时乙烯基双键转化率达97.6%;固化膜具有很好的柔韧性、耐冲击强度及附着力,具有较好的硬度及耐酸、耐碱、耐盐、耐水性。

关键词: 树脂酸烯丙酯, 紫外光固化, 反应性能

Abstract: Properties of cured product and affecting factors of the reaction were researched using allyl resinate as monomer. Conversion rate of vinylic double bonds was characterized and detected by FT-IR analysis and mechanical properties of cured films were detected. Results showed that conversion of double bonds first increased and then decreased with the increase of the dosage of initiators, and increased with the increase of irradiation time. Surface drying time became shorter, that is, relative curing speed became faster with the increases of dosage of initiator and irradiation intensity, and the decrease of lamp distance. At lamp distance 4.5cm and irradiation intensity 100%, conversion rate of vinylic double bonds was 97.9% using irradiation time 250s with 8% of MK, while conversion rate was 97.6% using irradiation time 300s with 5% of Darocure 1173 as photoinitiator. The obtained UV-cured coating possessed superior properties in flexibility, impact strength and adhesion, as well as good properties in hardness, acid resistance, alkali resistance, salt resistance and water resistance.

Key words: allyl resinate, UV curing, reactivity